Sensitizing Paste for Electroless Nickel Deposition

I am seeking a paste that can be used as a catalyst for electroless nickel deposition onto ceramic. The paste should have a low ash content, a viscosity of 1,000 to 10,000 cps and contain precious metal at a low concentration to minimize expense. Please let me know if anyone has a suggestion.

Michael Boudreaux
- New Orleans, Louisiana

topic 88 is a start...

Ted Mooney, P.E.
Striving to live Aloha
finishing.com - Pine Beach, New Jersey

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: