Microetch of Copper

2001

I am now plating EN on copper substrate with very small size. The iso-tropic etching of copper is not suitable for my application. Anyone know how to turn the isotropic etching to anisotropic etching?

Thanks for your attention.

Yin Xiong
- Singapore

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: