PROCESS FOR BETTER CORROSION PROTECTION

PLEASE GIVE ME THE PROCESS INFORMATION ABOUT CATHODE CHROME PASSIVATION OF NICKEL / CHROMIUM PLATED COMPONENTS FOR BETTER CORROSION PROTECTION ON OUR STEEL PARTS.

Ishtiaq Hussain
ENGINEERING & METAL WORKS - Karachi, Sindh, Pakistan
2001

That's a new one on me, Ishtiaq. Sorry, I've never seen or heard of putting anything on after the chrome.

Ted Mooney, P.E.
Striving to live Aloha
finishing.com - Pine Beach, New Jersey
2001

Mr Ted and Mr Ishtiaq Hussain:

Yes, the dichromate cathodic treatment produce more protection for nickel-chromium plated articles. For more details you can find information in

Nickel and Chromium Plating [on Amazon affil links], j.k.Dennis page 301-302

Hope that will help.

Regards

Anas
- Damascus, Syria
2001

Thanks, cousin Anas.

Ted Mooney, P.E.
Striving to live Aloha
finishing.com - Pine Beach, New Jersey

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.