Is Chrome Steel tubing Resistant to 350 °C Hydrogen?

Q. Hi. I have a question regarding the resistance of Cr-Steel tubing under hydrogen flow at 350 °C for several days or weeks. Is there some experience about this topic around?

DOMINGUEZ Jose
Energy & Oil - Mexico City; D.F.; Mexico
January 10, 2018
publicly reply to DOMINGUEZ Jose

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: