Can a Dip Brazed Aluminum Chassis Be Hard Anodized

Q. As the title asks: Can a 6061 aluminum chassis that has been dip brazed be hard anodized? The filler is aluminum so it seems like it should be possible but I don't know if trapped salts would be an issue. In addition, this chassis must meet IP67. If it can be done, what issues can I expect?

Dan Timmons
Product Design - Endicott, New York
September 13, 2012

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: