E-coat over Cadmium plating: How and Why

Q. I work for a contract painting company that supplies e-coating and powder coating services. We have customers that will send us parts that have a Cadmium plated coating or a Zinc/Nickel plated coated and request an e-coat finish over the top. Since we're not able to process the parts through the normal processing/cleaning stages as they will remove the base coating that has been applied to them, we have problems getting consistent results. Can anyone provide some insight as how to address this and explain what benefits the customer would realize from trying to have this base coatings under the e-coat? Thanks

Rick O [last name deleted for privacy by Editor]
- Mayville, Wisconsin, USA
June 19, 2012

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: