Stainless Steel Grades for Turbocharged Exhaust manifold

I would like to know which SS Grade can withstand upto 1000 °C exhaust temp. This is for fabricating exhaust manifold which can be bendable and welded easily.

Siddharth Rao
R&D Engineer - India
October 31, 2011

You might get away with type 446. However, why not use CF8C-plus which is proven for this application?

Jeffrey Holmes, CEF
Spartanburg, South Carolina
November 7, 2011

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: