Stainless Steel Grade that's attracted to but won't become a magnet?

October 14, 2011

Hi,

Does anyone know of a stainless steel that won't become a magnet (i.e. won't attract a non-magnetized piece of iron), but that itself will be attracted to a magnet.

Thanks.

Josh Colton
Engineer - Santa Clara, California, USA

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: