Hydrogen bakeout of a 5" thick F22 2 1/4 1Mo part

Hi
What temperature should we use for hydrogen bakeout of a 5" thick F22 2 1/4 1Mo part ?

James Strickler
Weld shop - Houston, Texas
August 30, 2011

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

Finishing
Jobshops Capital
Equipment Chemicals &
Consumables Consult'g,
& Software