Electroless Nickel Plating vs. Yellow Chromated Aluminum's Thermal Conductivity

I am looking for the thermal conductivity for Electroless Nickel Plated (MIL-C-26074, ASTM B733) Aluminum (6061-T6)and the thermal conductivity for Yellow Chromated (MIL-DTL-5541-F ASTM B449) Aluminum (6061-T6)?

Trying to see how close there are and which one is better thermally.

Benjamin Lee
Product Designer - Brockton, Massachusetts, USA
August 12, 2011

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: