I want to know what are the steel compositions suitable for hot-dip galvanizing?

Sreedhar Patnaik
employee - Visakhapatnam, Andhrapradesh, India
February 28, 2011

April 20, 2011

Sir:

Many, many types of steels are galvanized. Most economically galvanized steels are rather low in silicon, phosphorus, copper, and aluminum. All of these types of steels are more reactive toward the zinc and usually result in thick gray zinc coatings.

There are additives for the molten zinc that reduce the zinc coating thicknesses on the steel.

Regards, Dr. Thomas H. Cook, Hot Springs, South Dakota, USA

Dr. Thomas H. Cook
Galvanizing Consultant - Hot Springs, South Dakota, USA

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: