Corrosion/rust in welded area of SS316L swimming pool brackets

Very good day

We fixed a supporting bracket with grab rails in swimming pool which has salt chlorination system. Within a few days supporting brackets got rust/corossion/brown colour formed on welded area and spread all over area in brackets.

Supporting bracket has one base plate, Rod and Pipe holder. Here, Rod and Base plate then Rod and Pipe holder has been welded by tungsten inert gas welding using filler rod, 316 L.

Please help us how to avoid the corossion/rust in brackets.

Is there any reason that water in swimming pool not balanced will be affect the Stainless Steel.

Abdul Kader
Site Engineer - Ruwi, Muscat & Oman
February 16, 2011

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: