Tin plating gray deposits

March 7, 2010

I am plating Fe Terminals but after nickel, coopper I apply Tin but 3KG is taking me 44 mins at 7.5V

Sometimes I get a bright finish but sometimes there is not brightness the pieces looks like with dust on surface.

Do you know why?

Sergio Samaniego
Mexicali, Baja California, Mexico

Hi, Sergio. 3KG? What does 3KG mean?

Regards,

Ted Mooney, P.E.
Striving to live Aloha
finishing.com - Pine Beach, New Jersey
March 8, 2010

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: