Contact material for Corrosion Resistance to Salt Water and Chlorine Water

My company is developing an electronic product for swimming. The charging contacts will be exposed to ocean salt water as well as salt and chlorine pool water.

What would be the best material / finish to resist corrosion?

Todd Zeilinger
Product Designer - Holland, MI, USA
December 18, 2009

Hi, Todd. I would think electroless nickel is appropriate.

Regards,

Ted Mooney, P.E.
Striving to live Aloha
finishing.com - Pine Beach, New Jersey
December 18, 2009

You need enclosure? What part should be protected from corrosion?

Shanmugavel Thangappan
- Madurai, Tamil Nadu, India
January 6, 2010

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: