Problem in silicate base trivalent passivation

we are doing alkaline zinc with trivalent passivation.it is 3rd generation passivation.I am facing white patches after passivation. I am using all D.I water rinse in passivation line.the patches are removing if I rubbish with cloth.where is the problem,kindly give your suggestion

Shankar Shankar
plating shop manager - India
October 23, 2009

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: