Production Zinc Plating to related specifications QQZ325 or ASTM B633

We use Zinc Plating on a daily basis, we are looking for some explanation of how to address the need for touch up of a faraday cage condition minimizing deposit thickness in corners and recess where a secondary anode would not be practical. Is use of a cold galvanizing compound Cold Galvanizing Compound / Zinc Rich Paint allowable by these Zinc Plating specs, QQZ235 and ASTM B633?

Michael Riley
Buyer of Plating services - North Salt Lake, Utah
April 10, 2009

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: