Red residue problem with conventional hot black oxide (280 - 290 F)

We recently installed a Black Oxide Tank. First we processed 10 parts, coating was good, after that we processed 3 parts coating was excellent, but after that we tried 20 parts and we observed red residue and black coating was light. Can some one identify the problem and suggest the solution? Thanks

Vijay Kansupada
Buyer - Columbia, SC
February 5, 2009

Different material often own different color , you are sure of your parts' material? in addition, too high temperature often lead to some question you talked

Jack Zhao
metal finishing - Shenzhen, China
February 16, 2009

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: