Brass base material plated with silver over copper

When I bake parts at 260 deg C it turned green. Can anyone tell me what is wrong?

Thanks,

Mike Balbuena
- Orlando, Florida
2007

The copper is migrating thru the silver. You need to use a nickel strike. I think that a sulfamate strike will work better on copper than a Woods strike. A Watts nickel with the pH lowered might work well also.

James Watts
- Navarre, Florida
2007

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: