How to strip TiAlN from high speed steel




How to strip TiAlN form high speed steel? I'm using H2O2 +NaOH +H2O + EDT, but the time is long ( > 10 hours).

Ronaldo Ruas
Resarch / Process Engineer - São Paulo, São Paulo, Brasil
2007



2007

Dear Ronaldo Ruas,

hi!

Have you tried different proportions of the alkaline and H2O2? In my experience, it can decoat the coating is not very long. Maybe because of your coating's thickness.

By the way, I am a crazy football fan of Inter Millan and Argentina, so your name is really sensitive to me. I am kidding of course :)

Wayne Xue
- SHENZHEN, CHINA




(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

Finishing
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g,
& Software


About/Contact  -  Privacy Policy  -  ©1995-2025 finishing.com, Pine Beach, New Jersey, USA  -  about "affil links"