304 SS corrosioned by low pH DDBSA @ 80C

Could you please tell whether there is corrosion of 304 SS tank used by a low pH DDBSA (Dodecyl Benzene Sulfonic Acid pH=2~3) at 80C for 8hrs?

Harris Shang
GE (China) R&D; Center - China
2007

2007

Hi there,
It will attack the metal over time where there are welds.
In fact if you use a magnet on the welds it will stick to the metal.

Ken Foyn
- Durban, South Africa

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: