Nickel plating pretreatment

Like to know, what is the best pre-treatment for this material NdFe Grade N42SH
which require to plate NiCuNi at 18 microns for electronic industries.

Arthur Koo
Plating Shop - Hong Kong
2006

It will be easier to give you a correct answer if you will give the composition of the alloy.

Sara Michaeli
Tel-Aviv-Yafo, Israel
2006

2007

Sara,
Composition of this alloy NdFe Grade N42SH consist of neodymium (Nd) 30%, Iron (Fe) 66% and Boron (B)1% . Hope this help to answer my question.

Thanks,

Arthur koo
- Hong Kong

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: