Dull tin plating

We are using solderon acid bath for tin plating. In that we are facing a dull plating of tin immediately after a week of preparation of a new bath

J.Billy Joel
plating shop manager - India
2006

It could be due to imbalance of Solderon Primary & Secondary and/or organic contamination. Use hull cell or rotary cell to justify if carbon treatment and/or Solderon Primary/Secondary adjustment can help.

David Shiu
- Singapore
2006

Dear Mr.Joel,
Check the water quality to be used. It should be chloride free.

Harish Gurnani
- AHMEDABAD, GUJARAT, India
2006

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: