Titanium surface prep for organic coating

What is the best surface preparation to get an organic coating to stick to titanium? The typical HF based preparation does not seem to be getting the job done.

Emilio Giamatti

2006

Have you tried a fine abrasive blast?

James Watts
Navarre, Florida
2006

Part size and geometry does not permit abrasive blasting.

Emilio Giamatti

2006

Ed. note: Please list any other potential solutions that you have already eliminated due to part size and geometry or other considerations, Emilio. We realize it isn't intentional, but it is slightly inconsiderate to ask for help and then instantly dismiss people's efforts on your behalf.

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: