Chromic acid anodize can it be stripped and reworked without edging the aluminum

Parts got chromic acid anodized and were not finish deburring.
Can I deburr the parts and have the chromic acid anodize strip and re-anodize.

Angel Ruiz

2006

Yes you may strip and re-anodize but the original surface is now under the dimension of the original surface.

Robert H Probert
Robert H Probert Technical Services

Garner, North Carolina

2006

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: