Hardness of aluminium alloy after surface coating

2005

Dear sir,
How can I get the hardness of aluminium alloy after surface coating (anodizing Type-3, Class-2)? I hope your reply. please help me to solve (calculation or other standard specification).
thank you so much,

Saw Gyi
dms - Penang, Malaysia

Vickers Micro - Hardness Test: BS 5599: 1978(ISO 4516)

I hope this helps

Keshava Prasad M
- Chennai, India
2005

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: