AL 6061-T6 for demineralized water

Is a shell and tube heat exchanger with AL 6061-T6 tubes suitable for heating demineralized water from 50F to 200F or will there be a corrosion problem?

Ronald Messen
steam plants - Clifton Park, New York
2005

I don't know of anyone using an aluminum heat exchanger for DI water. Stainless steel is most commonly used.

Lyle Kirman
consultant - Cleveland Heights, Ohio
2005

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: