Tin plating humidity resistance

2005

HAI,

1)PLEASE LET US KNOW WHETHER BRIGHT ACID TIN PLATING WITHSTANDS ENVIRONMENTAL TESTING AT 65DEG. C & 90% RH FOR 300 HOURS.

2)IF YES WHAT ARE THE THICKNESS AND OTHER PARAMETERS TO BE MAINTAINED.

3) WHICH CHEMISTRY SUPPLIERS ARE CAPABLE OF OFERING THE SAME.

SE.RAMAMOORTHY
HYDERABAD LEXTECH LTD. - HYDERABAD, AP, INDIA.

2005

Dear Mr Ramamoorthy,

What is the substrate over which Tin is plated? A short answer is also NO for the 300 hours.

Khozem Vahaanwala
Saify Ind

Bengaluru, Karnataka, India

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: