Looking for a finish on low carbon steel which will not flake off during a crimp operation, looking to pass salt spray test no red rust at 96 hours.

Thanks,

Ken Brandt
HUSCO Automotive LLC - Waukesha, WI
2004

I would think that a correct zinc with an olive drab chromate might work and would be the cheapest option. Other options might be cadmium or silver and possibly electroless nickel. Preplate operations will need to be very well done and monitored to pass your no flake requirement.

James Watts
- Navarre, Florida
2004

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: