Torque - Tension for Dacromet

I am Design Engineer we are getting done dacrometing from our vendor for wheel bolts and other special fasteners, I want to know what will be the impact on torque - tension relationship of particular fastener as long as there is not any kind of H2 entrapment please suggest.

Prashant Akhare
- Pune, Maharashtra, India
2004

2004

The supplier of Dacromet materials, Metal Coatings International, can probably assist in the torque-tension issues.

The process itself probably will not contribute to hydrogen embrittlement, but necessary pretreatment might.

Ted Mooney, P.E.
Striving to live Aloha
finishing.com - Pine Beach, New Jersey

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: