Type of aluminum alloy for anodizing cathodes




We do sulfuric acid anodizing of aluminum. We are presently using aluminum anodes in our tanks and aluminum clamps to hold our sheet stock. What is the best aluminum alloy to use for this application. We use hydrofluoric acid for our sheet and rack strip. We are presently using 6061 alloy.

Ernie Burroughs
anodizer - Waukon, Iowa, USA
2004



6063 T-6 is the best to use for sulfuric acid anodizing.

Marc Green
Marc Green
anodizer - Boise, Idaho
2004




(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

Finishing
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g,
& Software


About/Contact  -  Privacy Policy  -  ©1995-2024 finishing.com, Pine Beach, New Jersey, USA  -  about "affil links"