Aluminum 6082-T6 vs. 6060-T66

2004

Dears Sirs,

I would like to know if there are tables of aluminum alloys 6060 T66 and 6082-t6, which have been tested by a CASS Salt spray test ISO 9227. We'd like to know which alloy has better resistance. I thank you in advance for an early reply.

Ron Bongers
productmanager - Almere, Flevoland, The Netherlands

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: