Regarding hot dip galvanising dross formation

Regarding process of hot dip galvanising please explain difference among top dross, bottom dross and zinc ash (wet flux process) and their source of formation and how to control them.

A Kothia
- Biratnagar, Morang, Nepal
2003

Hopefully someone will answer you soon, cousin Kothia. But we've found that the readers are more disposed to help inquirers who pose their questions in terms of their own real-world situation, so we urge you to please tell us what is going on. Thanks!

Ted Mooney, P.E.
Striving to live Aloha
finishing.com - Pine Beach, New Jersey
2003

Bottom dross is formed due to reaction of free iron particles on the strip and reaction of Zn with the iron of kettle,,,,
Top dross is formed due to oxidation of Zn due to contact with air,,,,

D K Jain
- NOIDA, UP, India
February 3, 2011

adv.
this text gets replaced with bannerText

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: