400 Micrometer Ni-P

2003

Dear sir,

Can I obtain 400 Micrometer Ni-P on Al-Si from electroless process?

Thank you,

Harouni
University - Esfahan, Iran

I have done some more research and even done some experimenting, although I think my current is to high and I am going to electronics store tomorrow to try to remedy that. I am now asking can I electroform lead with an acid-copper solution, basically forming a copper jacket for the bullet by building up of copper on copper.

Thanks,

Craig McAdam
hobbyist - Macon, Georgia, USA
2004

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: