Terminal void problem for chip resistor

2003

Hi,there.

My company is doing barrel plating for chip resistor which using nickel & solder plating. Sometime I face problem at terminal side having void which cause solderability problem. It looks like no nickel or low thickness nickel cause solder cannot plated. But why on top & bottom side, I never faced this problem only at side terminal. I suspect maybe nickel sludge cause the problem, so now I frequently wash the anode bag & anode itself to clear the sludge. I don't know whether this is the correct method to prevent "terminal void". Another question, for cleaning of anode bag, now I';m using HCl to wash the nickel anode bag. Solder anode bag I'm using city water to wash. Any chemical can apply on to make the anode bag more clean? Anyone can help me?

Thanks,

Loh Kok Yong
Electronic component - JB, Johor, Malaysia

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: