Rework on annealed radiometal rods

Part of material has been removed for the radio metal (50% Ni-Fe) rod, which has been annealed one. Whether the part removed portion may rust?

Babu
relays - Tamil Nadu, India
2003

I'm not sure I've understood your question completely, but I say yes it will develop corrosion spots after awhile.

Khozem Vahaanwala
Saify Ind

Bengaluru, Karnataka, India

2003

adv.

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: