Coating / Plating exposed to Freon

Can anyone recommend a coating / plating for steel in a freon environment? The parts must withstand 5000 hours in freon at -40 F. Application: Hydrogen fuel cells.

Jack Arnolde
- Chicago, Illinois, USA
2003

I would expect electroless nickel to be fine.

Ted Mooney, P.E.
Striving to live Aloha
finishing.com - Pine Beach, New Jersey
2003

I would think that copper would be the way to go, since air conditioning systems are made with copper piping. Copper is also a very good heat dispersing material.

Dan Brewer
chemical process supplier - Gurnee, Illinois
2003

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: