Mil-F-14072 requirements

2002

Need to know if anyone is familiar enough with MIL-DTL-14072 [on DLA] to tell me what processing is involved with the e300 designation or if I need more information to correctly interpret the requirements.

Thanks to all.

Ken Gilliam
- Garland, Texas

E300 is passivation of stainless steel per ASTM ASTM A380 . The passivation will be dependent upon the type of stainless.

Wayne McKee
- Mississauga, Ontario, Canada
2002

March 20, 2009

CAN ANYONE TELL ME IF MIL-DTL-14072 [on DLA] E300 DICTATES A HIGH
HUMIDITY TEST OR ANY OTHER? (SALT SPRAY ETC)?

SOME VENDORS ADD A CHARGE FOR THIS SAYING IT IS A
REQUIREMENT. ALL THAT I READ WOULD SUGGEST TESTING IS ONLY
REQUIRED IF SPECIFIED ON PRINT OR CUSTOMER REQUESTS TESTING.
ACTUALLY, THE OLD QQ-P-35C [from DLA] SPEC SEEMS TO INDICATE THE SAME.

RICHARD GOULDMAN
MACHINE SHOP - RICHMOND, Virginia

www.finishing.com is made possible by supporting advertisers ...
this text gets replaced with bannerText

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: