Activating titanium prior to electroless nickel plating

I am looking for information on activating titanium prior to electroless nickel plating.

Bill Emery
- Tulsa, OK
2002

Nitric/HF 3 mins, no current, room temperature
wet Al blast, 60 grit
HCl/HF 15-20 seconds, no current, room temp
Rochell salt solution 1 min
CYANIDE Copper strike

M. Cera
- Oklahoma City, Oklahoma
2002

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: