Gold properties when plated from sulfite bath

Anybody can give me some idea of physical properties of plated gold from a sulfite bath? I am looking for information such as microhardness (HK or HV), youngs' modulus, etc. Thanks.

Hong Shen
- Thousand Oaks, California

"The Properties of Electrodeposited Metals and Alloys"
by William Safranek

on eBay or

AbeBooks

or Amazon

(affil links)

I would recommend that you purchase "Properties of Electrodeposited Metals and Alloys" a handbook, second edition, Wm H. Safranek author.

This will let you compare lots of different types of gold plate. This is a lifetime type reference book that should be had by any firm using electroplating.

James Watts
- Navarre, Florida

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.