Titanium Anodized Custom Implant

Dear All,

We have a custom implant which is very close to the skin surface. If we leave it in its natural state it will darken the skin very quickly. As this is a visable implant this is no good.

Material: Grade 2 Titanium.

I have limited infomation on anodizing so if you can give enough infomation to carry out this process safely it would be appreciated.

Paul Morrison
- Christ Church, New Zealand

Paul, what color do you think is the best for the implant? We can provide you with the environmentally friendly anodizing solution to obtain the color you want. The range of colors available are on our web site.

Anna Berkovich
Russamer Lab

Pittsburgh, Pennsylvania

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: