Q. Hi all,

I am currently doing a project "design a laboratory electropolisher for metallurgical specimen". It would be really appreciated if anyone could give me some basic knowledge about:

1.Analysis of existing solution
2.Concept of design
3.Calculation and design
4.How to build a polisher

Thanks for your help

Best regards,

Adrian Kelly
- Bris, QLD, Australia

A. Hello Adrian!

If you are interested in metallographic electropolishing and want more information on that topic, I'd suggest you first (search under that topic in major search engines).

Good luck!

Lee Gearhart
metallurgist - E. Aurora, New York

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: