ZINC PLATING STRUCTURE

Dear all,

WHAT IS THE DIFFERENCE BETWEEN COLUMNAR STRUCTURE ZINC PLATING AND LAMINAR STRUCTURE ZINC PLATING. HOW THOSE PLATINGS WORKS. WHAT ARE ALL THE OTHER TYPES OF STRUCTURE OF ZINC PLATING. FROM WHICH TYPE OF PLATING WE CAN GET DIFFERENT PLATING STRUCTURE.

RAHUL
- DUBAI

All alkaline cyanide and non cyanide baths give a columnar structure. All chloride (acid) baths give you a laminar structure.

Khozem Vahaanwala
Saify Ind

Bengaluru, Karnataka, India

What lab evidence or scientific proof enabled you to make your conclusion?

George Hunter
- Ferndale, Michigan, USA

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: