Process in decorative chrome plating

2005

Our decorative chrome plating process is

Hot degreasing
Hot Electrolytic Degreasing
Pickling
Semi- Bright Nickel
Acidic Copper Bath
Bright Nickel
Chrome Bath

But someone told me that inside of using acidic copper bath, we can use semi-satin nickel bath
Someone know anything about that

Nafiz Arda Baþaran
Termosan Co. - Istanbul,Turkey

2005

Hello...
Sorry but I didn't understand exactly what you mean.Especially what is relationship between decorative chrome and your question.Anyway...I know you plate towel warmers.I think you want to know can I plate semi-bright plating instead of acid copper plating.Of course its possible but I never heard semi-satin nickel.Also its very strange this name because satin nickel also dull deposit.How can it be dulled ? I don't know.So,you can use semi-bright or double even multiple system instead of acid copper plating.

Good Luck.............

emre tuna
- Turkey

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.